Effect of Molybdenum on Microstructure and Mechanical Properties of Grey Cast Iron

The influence of molybdenum addition on carbide precipitation, microstructural evolution, and tensile strength in grey cast iron was systematically investigated. Experimental results demonstrate that molybdenum significantly modifies graphite morphology while refining pearlite structure through carbide formation mechanisms.

1. Graphite Characteristics

Molybdenum addition effectively modifies graphite morphology in grey cast iron:

Mo Content (%) Graphite >300 μm (%) Graphite <100 μm (%) Count/mm²
0.034 13.8 50.0 118
0.260 7.2 54.8 145
0.560 3.1 58.3 172
0.770 2.1 61.5 197

The relationship between molybdenum content and graphite length reduction can be expressed as:

$$ L = L_0 \cdot e^{-k[Mo]} $$

Where \( L_0 \) represents initial graphite length and \( k \) denotes the molybdenum influence coefficient (0.45 mm⁻¹).

2. Pearlite Structure Evolution

Molybdenum demonstrates dual effects on pearlite formation in grey cast iron:

Parameter 0.034% Mo 0.770% Mo Change
Pearlite Content (%) 95.01 89.85 -5.4%
Interlamellar Spacing (nm) 395 229 -42%

The refinement of pearlite lamellar spacing follows the relationship:

$$ \lambda = \frac{C}{[Mo]^{0.33}} $$

Where \( \lambda \) represents interlamellar spacing and \( C \) is a material constant (627 nm·wt%¹/³).

3. Carbide Precipitation Mechanism

Molybdenum promotes carbide formation through three distinct mechanisms:

  1. Eutectic carbides at grain boundaries
  2. Intragranular secondary carbides
  3. Composite (Mo,Cr)23C6 carbides

The carbide volume fraction increases linearly with molybdenum content:

$$ V_c = 0.015 + 2.5[Mo] $$

Where \( V_c \) represents carbide volume percentage and [Mo] is molybdenum concentration in wt%.

4. Tensile Strength Enhancement

Mechanical property improvements in grey cast iron correlate with microstructural changes:

Mo Content (%) UTS (MPa) Hardness (HB) Elongation (%)
0.024 254 187 1.8
0.800 368 241 1.2

The tensile strength enhancement follows a logarithmic relationship:

$$ \sigma_{UTS} = 250 + 150\log(1 + 10[Mo]) $$

This equation demonstrates diminishing returns at higher molybdenum concentrations (>0.8 wt%).

5. Phase Transformation Kinetics

Molybdenum significantly affects the pearlite transformation kinetics in grey cast iron:

$$ t_{0.5} = t_0 \cdot e^{\frac{Q}{RT}} \cdot (1 + 3.2[Mo]) $$

Where \( t_{0.5} \) represents 50% transformation time, \( Q \) is activation energy (215 kJ/mol), and \( R \) the gas constant.

6. Industrial Application Considerations

Optimal molybdenum addition for automotive components balances performance and cost:

Application Recommended Mo (%) Typical UTS (MPa)
Brake Drums 0.5-0.7 320-360
Cylinder Blocks 0.3-0.5 280-320
Gear Housings 0.2-0.4 260-300

The comprehensive strengthening mechanism in molybdenum-modified grey cast iron combines:

$$ \Delta\sigma_{total} = \Delta\sigma_{graphite} + \Delta\sigma_{pearlite} + \Delta\sigma_{carbide} $$

Where each strengthening component contributes approximately 35%, 50%, and 15% respectively to the total strength improvement.

This systematic investigation provides quantitative relationships for optimizing molybdenum addition in grey cast iron production, particularly for high-stress automotive components requiring enhanced mechanical performance while maintaining castability and cost-effectiveness.