Production of dual phase steel castings by sand casting
1. Production of heat subsidy for sand casting Mix the powdered heating material and binder evenly according to the required […]
Scientific
Scientific
Scientific
Design of exhaust system for sand core in sand mold casting
The reasonable design of the exhaust system of sand mold casting sand core should comprehensively consider the exhaust hole and
Scientific
Design of exhaust system for sand casting cavity
The design of exhaust system of sand mold cavity can be divided into three parts: pouring riser, air outlet, air
Scientific
Surface microhardness of gray cast iron after graphite annealing
The hardness changes of gray cast iron after laser melting and impact at different annealing temperatures are shown in the
Scientific
Mold filling and solidification characteristics of lost foam casting
Compared with ordinary sand casting, the solidification characteristics of lost foam casting are also different, mainly in the following aspects:
Scientific
Solidification simulation and process optimization of sand casting for large bearing pedestal
Through the analysis of the physical parameters of the sand mold casting, it is determined that the quality of the
Scientific
Casting process of lost foam casting empty shell
1. Foam casting for lost foam casting The molding of polystyrene bead mold can increase the foam density for improving
Scientific
Effect of laser shock on graphitization nucleation of gray cast iron
The nucleation and growth of gray cast iron graphite are gradually formed during heating. The nucleation position of gray cast
Scientific
Sand mold casting process design of large bearing pedestal
The material of the bearing seat is ZG310-570, and the production nature is mass production. 1. Sand casting process scheme
Scientific
XRD of the fused layer of gray cast iron after laser shock
The X-ray diagram of the surface of gray cast iron sample after laser shock melting is as follows. It can
Scientific
Sand mold casting technology of large bearing pedestal
Large bearing pedestals are used in power plants, petrochemical, metallurgy, shipbuilding and equipment manufacturing industries, such as steam turbine rotor
Scientific
Hardness test of lost foam casting rod mill liner
The figure shows the hardness of ZGMn13 and zgmn17 under different water toughening treatments. It can be seen that the
Scientific
Original technology of lost foam casting nodular cast iron reducer housing
The combination process of lost foam casting nodular cast iron reducer shell is shown in the figure. The design process
Scientific
Defects and control of nodular iron crankshaft in wet sand casting
The wet sand mold casting process of nodular iron crankshaft is mainly divided into two parts: sand mold preparation and
Scientific
Liquid shrinkage solidification of nodular cast iron
For the liquid shrinkage of nodular cast iron, the macro performance is the decline of molten iron liquid level, and
Scientific
PLC control of mold filling speed of sand casting machine bed
1. PLC software design PLC control software includes interface management program and monitoring program. The interface management program is connected
Scientific
Solution to the casting porosity defects often occurred in iron mold sand coated casting process
1. Increase the gate section size in the gating system Gate size in main core: changed from 33.5 / 34.6
Scientific
Research status of wear resistant cast iron
1. Ordinary white cast iron Ordinary white cast iron can only be used in as cast state, and carbon atoms
Scientific
Test verification and data analysis of nodular cast iron based on magma simulation software
1. Test scheme design Select specific nodular cast iron and specific process as the test object (as shown in Figure
Scientific
Simulation results and analysis of shrinkage porosity and shrinkage cavity in sand casting of mud pump body
Shrinkage porosity and shrinkage cavity are the most common defects in the process of sand casting, and they are also
Scientific
Iron mold sand coating process and common quality problems in original mold casting
1. Original mold design structure The original mold structure design of t9000-c iron mold sand coated casting cylinder block in
Scientific
CAE simulation and analysis of nodular iron castings of small motor base
In order to reconfirm the defects of the nodular iron casting and the rationality of the analysis results, the CAE
Scientific
Original technology and existing problems of rapid casting of tractor gearbox shell
1. Casting process In order to ensure the smooth filling of molten iron and prevent the occurrence of defects such
Scientific
Analysis on solidification process of mud pump body in sand casting
The three-dimensional models of casting, sand mold and cold iron are meshed by finite element method. After being imported into
Scientific
Characteristics and analysis of blow hole defects in motor shell casting
Through the verification of small batch production, from the statistical table of defects, the first defect type is blow hole
Scientific
Rapid casting and pouring test of tractor small parts
1. Water glass sand mold pouring test Figure 1 shows the water glass sand mold pouring test of the brake
Scientific
Test results of centrifugal casting isothermally quenched ductile iron bushing
Six groups of samples were selected and tested for mechanical properties by wav-600a universal testing machine. The results are shown
Scientific
Simulation results and analysis of gating system of mud pump body in sand casting
Figure 1 shows the simulation results of filling sequence and velocity field of each part of mud pump body in
Scientific
Analysis of mold filling process of mud pump body in sand mold casting
In order to evaluate the rationality of the optimized process scheme, the software ProCAST needs to be used to simulate
Scientific
Casting and casting of complex tractor parts
Compared with the traditional wood mold turning process, the mold size and size are limited by the table size and