Sand casting technology of motor shell steel casting
The weight of the steel casting of the motor shell is 381kg, which is similar to the barrel structure. The […]
News
News
Defect analysis and process optimization of sand casting of steel castings
In view of the serious casting defects in the small batch production process of ZHY Casting motor shell steel castings,
News
Hot crack defects of furan resin sand casting motor shell steel castings
The formation mechanism and influencing factors of hot crack casting defects are very complex. So far, there are three main
News
Furan resin sand casting motor shell steel castings
The name of furan resin sand comes from furan no bake process in English. Furan resin sand casting is a
Scientific
Casting technology of steel castings for motor housing
In 2020, the international and domestic economy went down seriously, the domestic foundry industry was in great depression, and many
Scientific
Formation mechanism of MNS inclusion defects in steel castings
The two kinds of MNS inclusion defects observed are formed on the surface of oxidized inclusions. According to the literature
Scientific
Microstructure and chemical composition of MNS inclusion defects in cast steel
Two different MNS inclusion defects were observed in cast steel. Fig. 1 shows the microscopic morphology of the first MNS
Scientific
New technology to reduce carburization of lost foam casting steel castings
At present, the new technologies and methods to reduce the carburization of steel castings mainly include negative pressure combustion empty
Scientific
MNS inclusion defects in steel castings
The material studied is low alloy steel, and its main alloy elements are common elements such as C, Si, Mn,
Scientific
Characteristics of slag inclusion and sand hole defects in medium and large steel castings
Fig. 1 slag inclusion defect on the upper surface of medium and large steel castings after processing, which is visually
News
MNS inclusion defects in steel castings
The non-metallic inclusions in molten steel during smelting and pouring are one of the important causes of cracks in steel
Scientific
Effect of pouring speed on insufficient pouring defects of investment casting
Unreasonable pouring speed setting of investment casting will also produce insufficient pouring defects. In order to determine the reasonable pouring
News
Design of sand casting gating system for mud pump body
The sand casting gating system of the mud pump body is not only the channel for the metal liquid to
Scientific
Slag inclusion casting defects in lost foam casting of steel castings
Slag inclusion casting defect refers to the casting defect formed by dry sand, coating and other inclusions as molten iron
Scientific
Analysis method of insufficient pouring defects of investment casting steel
Another investment casting thin-walled steel casting of ZHY casting was under poured in the trial production process, and the defects
Scientific
Repair of casting defects of medium and large steel castings
Different from forged steel parts, steel castings for hull structure have low carbon content and good welding performance. Defective parts
Scientific
Characteristics of porosity and shrinkage defects in medium and large steel castings
Fig. 1 the visual characteristics of air hole defects on the upper surface of steel casting hub are round, the
Scientific
Effect of pouring temperature on insufficient pouring defects of investment casting steel
In the casting defect scheme, the actual pouring temperature is 1560 ℃, and the actual average pouring speed is 0.38
Scientific
Semi rough machining of sand casting mold template
Use the tool with diameter d = 30mm and bottom corner radius r = 2mm for semi rough machining, create
Scientific
Improvement of casting defects of bolster and side frame steel castings
1. Improvement measures 1.1 Inspection and control of molding sand performance While maintaining the original test items and requirements of
News
Sand inclusion and sticking defects of steel castings of bolster and side frame
Bolster and side frame are important running parts on the bogie of rail freight car. They bear the gravity of
News
Reducing the carburization of lost foam casting steel castings
The measures and methods to reduce the carburization of lost foam casting steel castings mainly include the following aspects: (1)
Scientific
Study on Carburizing defects of lost foam casting steel castings
The lost foam casting method is flexible and convenient in modeling and pouring, especially for products with complex structure. lost
News
Difficulties in the application of sand casting simulation
It is difficult to obtain accurate input parameters in sand casting simulation. For material properties, although sand casting simulation software
News
Casting defect inspection of medium and large steel castings
According to the thinking method of formulating the inspection standard of JCSS hull steel castings in Japan, medium and large
Scientific
Characteristics of cracks defects in medium and large steel castings
Hot crack: the crack is an irregular curve, the inner surface is rough and black brown iron oxide. Cold crack:
Scientific
Analysis of insufficient pouring defects of investment casting steel castings
The support size of a thin-walled steel casting is 400 mm × 310 mm × 270 mm, minimum wall thickness
Scientific
Improvement of insufficient pouring defects of investment casting
Because the exhaust rib is not set in the original scheme, the simulation shows that the gas pressure in the
News
Insufficient pouring defects of investment casting steel
In recent years, with the application of advanced technologies such as high-performance (steel, non-ferrous alloy, etc.) materials, CAE analysis and
Scientific
Porosity casting defects in lost foam casting of steel castings
According to the causes, the pores produced by lost foam casting steel castings are divided into the following four categories.