Defects in lost foam casting reverse spray casting of steel castings
During the pouring process, due to the excessive amount of gas released by the thermal decomposition of the gas mold […]
Scientific
Scientific
Local solidification time of sand casting coupling parts
The figure below is a cloud diagram of local solidification time of sand casting coupling parts. At 81 seconds, the
Scientific
Negative pressure cutting casting defects of steel castings in lost foam casting
Main reasons: when the sand box is under vacuum, the external air is sucked into the mold due to the
News
Application steps of sand casting simulation
The application of sand mold casting simulation should not only find out the causes of defects, but also put forward
Scientific
Carburizing casting defects of steel castings in Lost Foam Casting
Carburizing is one of the common casting defects in the lost foam casting process of steel castings. The carburizing casting
News
Lost foam casting of steel castings
Lost Foam Casting (EPC), also known as negative pressure full mold casting, has developed to a considerable scale since it
News
Effects of casting defects and structural dimensions of heat resistant cast steel liner on its properties
1. internal stress is generated during lining plate casting, resulting in cracks in lining plate; 2. the fracture of the
Scientific
Cylinder block casting riser
Chilled iron is the most commonly used chilling material to control the solidification of cylinder block castings. It can be
News
Improvement measures of heat resistant cast steel lining plate
1. To reduce and eliminate the stress concentration of the lining plate, the specific methods are as follows: during casting,
Scientific
Effect of chemical composition of heat resistant cast steel liner on its properties
The chemical composition of ZG35Cr24Ni7SiN material of heat-resistant steel casting is as follows: Brand C Mn Si Cr Ni Mo
Scientific
Defect optimization of sand casting coupling parts
The specific optimization measures are as follows: set annular external cold iron in sand core 2. The purpose of this
News
Development of casting simulation technology
For thousands of years, people have mainly solved engineering problems through trial and error, especially how to produce high-quality castings.
Scientific
Original casting process scheme of cylinder block
The upper half of the middle cylinder block for a certain type of steam turbine is made of ZG20CrMo, the
News
Steam turbine cylinder steel castings
The split flange of steam turbine cylinder block steel casting is the upper and lower half of the cylinder block.
Scientific
Analysis of cold crack defects in large steel castings
1. Manifestations of cold crack defects Under the joint action of welding stress and other embrittlement factors, the bonding force
News
Defects of heat resistant cast steel lining plate
The heat-resistant cast steel lining plate (ZG35Cr24Ni7SiN) is easy to crack, melt or even fracture during use, and has a
News
Characteristics and application of heat resistant cast steel lining plate
Heat resistant cast steel, model ZG35Cr24Ni7SiN, has good oxidation resistance, high strength, good toughness, good wear resistance, heat resistance, corrosion
Scientific
Defect optimization and result analysis of sand casting coupling parts
Considering the easy realization degree and economic factors of each measure, and using measures 2, 3 and 6, the numerical
News
Traditional casting defect analysis
Firstly, we take the shrinkage porosity defect in steel castings as an example to explore how the traditional foundry solves
Scientific
Analysis of undercut defects of large steel castings
1. Manifestations of undercut defects Undercut is the result of electric arc scouring or melting the base metal near the
Scientific
Fatigue test of casting defects in cast steel joints
1. Fatigue load loading In order to effectively test the influence of multiple casting defects on the fatigue performance of
Scientific
Fatigue analysis of casting defects in cast steel joints
Through the finite element calculation of fatigue strength and safety factor, the changes of fatigue performance caused by different casting
Scientific
Structural modeling of tubular truss bridge with cast steel joints
In order to effectively analyze the fatigue performance of cast steel joints in tubular truss bridge, a tubular truss bridge
News
Casting defects of cast steel joints
With the continuous improvement of China’s economic strength and construction level, various steel structure buildings with beautiful appearance, high reliability
Scientific
Cause analysis and optimization measures of defects in sand casting coupling parts
1. Cause analysis After preliminary analysis, it is concluded that the main problem in the simulation results of tooling gating
News
The causes of billet continuous casting defects are analyzed
The defects of billet continuous casting mainly include surface defect reconnection, inclusion and scar, scratch and vibration mark. The internal
Scientific
Analysis of blowhole defects in large steel castings
1. Expression form of pore defect During the welding process, the gas in the molten pool does not escape in
News
Sand casting of dredge pump body
China’s dredging industry has a long history. As early as the spring and Autumn period and the Warring States period,
Scientific
Verification and effect of measures for casting defects of wheel hub steel castings
In order to verify the casting quality effect after process optimization, the trial production of 5 wheel hub steel castings
News
High strength gear ring steel casting
Low alloy high strength steel is widely used in mechanical engineering, electric power, pressure vessel, automobile industry, mining machinery, oil