nodular cast iron

Table 1 shows the impact absorption energy of nodular cast iron V-notch samples at different ambient temperatures. The samples are […]

1. Chemical composition detection Arl3460 direct reading spectrometer is used for chemical composition detection, and the chemical composition detection results

1. Molding sand properties In order to ensure good surface quality of castings, the performance of green molding clay sand

1. Layout design Disa230b vertical parting boxless injection molding machine is adopted, and the size of molding machine plate is

It can be seen from the table that the tensile strength and impact toughness of nodular cast iron show high

In order to minimize the content of harmful elements, the selected raw materials should be relatively pure, so high-quality pig

At different austenitizing temperatures and isothermal temperatures, the bending fatigue test results of ductile iron specimens at room temperature are

The tensile test shall be carried out in accordance with gb/t 228-2002 tensile test method for metallic materials at room

As cast crankshaft castings with nodular cast iron trademark of QT800-2 are selected as the samples. After testing, the nodularity

By controlling the size and distribution of graphite diameter and the spherical regularity of graphite, the correlation degree with the

The figure is the matrix structure diagram of the vibration lost foam casting ductile iron, in which figures (a) –

Fig. 1 (a) and Fig. 1 (b) show the hardness and strength changes of three groups of nodular cast iron

Figure 1 shows the graphite morphology of the nodular cast iron by vibration lost foam casting, in which figure 1

Fig. 1 shows the microstructure SEM of three groups of ductile iron samples. It can be seen from the figure

The figure below shows the graphite morphology at different wall thicknesses of lost foam casting ductile iron. Figures (a) –

Under normal circumstances, the number of graphite balls in nodular cast iron will affect the matrix structure and stress distribution

As the nodular cast iron treated at 1560 ° C has been obviously white cast, it is not satisfied with