Position effect of eutectic solidification of chromium white cast iron under pressure
The results show that the pressure, fluidity and cooling rate of liquid metal at different positions are different during solidification. […]
Scientific
Scientific
Scientific
Theoretical model of eutectic growth of chromium white cast iron under pressure
The stability of solid-liquid interface affects the morphology of microstructure and determines the final properties of materials. The expression of
Scientific
Effect of pressure on solute diffusion coefficient of chromium white cast iron
The relationship between pressure and solute diffusion coefficient can be described as follows Where: DP — solute diffusion coefficient under
Scientific
Eutectic growth mechanism of chromium white cast iron under pressure
Through the characterization and analysis of the morphology of the above hypoeutectic alloy 1 # eutectic structure, the eutectic morphology
Scientific
Effect of solidification pressure on eutectic content and size of chromium white cast iron
Because the primary phase in the solidification structure of alloy 1 is austenite, the eutectic austenite in the divorced eutectic
Scientific
Effect of solidification pressure on eutectic spacing of chromium white cast iron
Through the quantitative characterization of eutectic structure under different pressures, it can be seen that the morphology of each phase
Scientific
Effect of solidification pressure on eutectic morphology of near eutectic chromium white cast iron
The metallographic structure shown in the figure is the metallographic structure photo of near eutectic alloy 2. It can be
Scientific
Solidification test and mechanical properties test of chromium white cast iron by pressure casting technology
1. Hardness test (1) Macrohardness Thbrv-187.5 electric broville hardness tester is mainly used for macro hardness analysis of samples. As
Scientific
Microstructural analysis method for solidification test of chromium white cast iron by pressure casting technology
1. Sample preparation (1) Sample grinding and polishing Use pg-2da metallographic sample polishing machine to pre grind the sample with
Scientific
Experimental process of solidification structure of chromium white cast iron by pressure casting technology
1. Alloy melting The alloy was melted in 500 kg medium frequency induction furnace in air atmosphere. The raw materials
Scientific
Test equipment for solidification structure of chromium white cast iron by pressure casting technology
The main equipment of pressure casting experiment includes liquid die forging machine, special concave convex die, pouring ladle and pouring
Scientific
Material selection for solidification structure test of chromium white cast iron by pressure casting technology
The raw materials used in the experiment are two kinds of alloy composition, including low chromium hypoeutectic white cast iron
Scientific
Solidification structure of chromium white cast iron was modified by pressure casting technology
The purpose of this study is to modify the solidification structure of chromium white cast iron by pressure casting. The
Scientific
Research status of pressure casting of chromium alloys
The solid-liquid phase transition process changes greatly under pressure. With the increase of the temperature of the solid-liquid phase line,
Scientific
Effect of solidification parameters on Microstructure of cast chromium alloy
The effects of pressure on solidification structure, including nucleation rate, undercooling and diffusion coefficient of alloy elements, provide a good
Scientific
Effect of pressure on solidification of cast chromium alloy
The solidification process can be regarded as a binary system with solid-liquid two-phase equilibrium. The degree of freedom of the
Scientific
Study on tool Wear of PCBN Cutter in Milling vermicular Graphite cast Iron
Many studies have shown that the tool life of cutting vermicular graphite cast iron is 1/10 of that of cutting
Scientific
Application and control of casting coating density
Uniform and stable coating composition is the basis to ensure the coating process performance, which belongs to static control for
Scientific
According to the casting defects of gray cast iron cylinder body, type selection and coating formulation are developed
For different casting defects (such as sand sticking, porosity, sintering, veining, shrinkage porosity at hot spot, etc.), the foundry should
Scientific
The coating for gray cast iron cylinder block is selected according to the core assembly process and sand core
The gray cast iron cylinder body adopts the traditional horizontal pouring process, the sand core is dipped with coating respectively
Scientific
Optimization and simulation analysis of casting process
1. Defect analysis of original process plan In the original process, two blind risers are set at positions a and
Scientific
Basic information of casting product for a high class valve body
1. Product structure and technical requirements The diameter of valve body is ϕ 254 mm, the maximum outline size of
Scientific
Improvement of casting process for automobile clutch flywheel
1.Runner 2. Runner cup 3. Riser 4, 5, 6. Ingate 7. Lap sheet 8. Sprue 9. Annular runner The original
Scientific
Analysis of slag inclusion in brake shell produced by Lost Foam Casting
1.Current process Due to the serious slag inclusion problem, the white mold material is replaced by stmma, the specific gravity
Scientific
Improvement of casting process for excavator guide wheel
1、 Improvement measures for defects such as sand hole and air hole are as follows. 1) Properly increase sand mold
Scientific
Analysis of casting process of excavator guide wheel and confirmation of main factors
Through the analysis of the failure parts by using the main factor diagram method, the causes of the fracture of
Scientific
Riser design of high carbon steel roll casting
Riser is a kind of structure for storing liquid metal in the mold, which is used to compensate the possible
Scientific
Riser design of high carbon steel roll casting
Through the observation of the defects, it is found that the defects are shrinkage porosity and shrinkage cavity, which are
Scientific
Finite element analysis of casting process scheme for extra large crusher frame
1. Static structural analysis Finite element static structural analysis is carried out for the box type and deep cavity type
Scientific
Scanning detection process and image generation of casting water cooled shell sample
After the sample navigation is completed, the detection can be started, as shown in Figure 1. Move the sample table