What about casting coating without film
If the die is not hung, it means poor coating and hanging. The reasons for poor coating and hanging should […]
News
News
News
Engine casting cylinder block and head
With the rapid development of China’s automobile manufacturing industry, many high-end automobile brands have been launched almost at the same
News
Improvement measures for loose and under cast defects of regulating and sealing pieces
In the process, the asbestos is wrapped on the mold shell for treatment (as shown in Figure 5), that is,
News
Prevention methods of shrinkage cavity and porosity in cast iron
Features: in the thick section of the casting, hot spot or axis and other places of the final solidification, rough
News
Characteristics and remedy of under casting defects in sand casting
Defect characteristics and detection methods It shows that the sharp angle, edge angle, thin section and narrow gap of the
News
Effect of water-based zircon powder flow coating performance
When the dosage of HB type suspending agent is 1 phr, the suspending property has reached 97%. The surface strength
News
The slag inclusion in ductile iron casting
There are three types of slag addition: the first type of coarse slag is 2mg · SiO2 + MGS or
News
Prevention and treatment of the subcutaneous porosity in ductile iron casting
The following measures can be taken: (1) When wet casting is adopted, the moisture content in the sand must be
News Scientific
Features, causes and prevention of the uneven hardness and coarse graphite defects of the castings
Features: Coarse graphite: the size of graphite in the metallographic structure is very large, or there is massive graphite, and
News
Characteristics and remedy of cold crack and warpage in sand casting
Defect characteristics and detection methods 1.Cold crack It is also a straight or curved crack on the surface of the
News Scientific
Defect characteristics, causes and prevention of lower core of casting
Features: Poor lower core (core deviation, core dropping, sand squeezing and core breaking) Causes: A. Mask is not adjusted well,
News Scientific
Analysis on the defects of loose and under cast thin wall castings
When the wall thickness of high-temperature alloy castings such as adjusting piece and sealing piece is changed from 1.1mm to
News
Characteristics and remedy of hot crack in sand casting
Defect characteristics and detection methods It is a straight crack on the casting. The surface of the crack is strongly
News
The phenomenon and cause of air hole under the skin of ball milled cast iron
Phenomenon One of the most common defects in the production of nodular cast iron is subcutaneous porosity. Subcutaneous porosity is
News
Characteristics and remedy of shrinkage defects in sand casting
Defect characteristics and detection methods 1.External shrinkage cavity It is a depression exposed on the casting. The rough formation of
News
Characteristics and remedy of slag inclusion in flux of sand casting
Defect characteristics and detection methods The dregs are dark brown and irregular in shape near the inner gate and the
News Scientific
Characteristics, causes and prevention of casting white edge defects
Features: The white cast is hard and brittle, and it is difficult to break and turn white Causes: A. Casting
News
Casting shrinkage defects in engine cylinder block and cylinder head
The structure of cylinder block (cylinder head) casting is complex, and the wall thickness is quite different. The thick and
News
Features, causes and prevention of casting connection defects
Features: After removing the riser, there is less meat in the neck of the riser. Causes: The shape and size
News
Shrinkage and porosity defects of ductile iron casting and their prevention
The shrinkage porosity and porosity are more common in ductile iron than in ordinary gray iron. To prevent them, more
News
Defects in the material properties of the engine cylinder block and cylinder head
Throughout the development trend of engine technology at home and abroad, we are pursuing to reduce the wall thickness of
News
Characteristics, causes and prevention of casting porosity
Features: Invasive pore: the pore size is generally large, in the shape of round, ball or pear; the pear shaped
News
Characteristics of die casting process
Die casting is a kind of metal mould pressure casting on die casting machine, which is the most efficient casting
News
Internal casting defects of die casting (part 2)
6 Non metallic hard point (1) Features and inspection methods: In the process of machining or after machining, the appearance
News
Defect characteristics and remedy of honeycomb in sand casting
Defect characteristics and detection methods A wormhole or loose hole appearing in the thick part of a casting or in
News
The bad spheroidizing defect of ductile iron casting and its prevention
The bad spheroidization means that the spheroidization does not achieve the expected effect. The metallographic structure of poor spheroidization is:
News
Characteristics, causes and prevention of shrinkage cavity and porosity in casting
Features: Shrinkage cavity: the hole with large volume, rough wall surface and irregular shape in the casting Shrinkage porosity: a
News
Other defects of steel casting and preventive measures
1.Deformation Long and plate castings are easy to deform. After some castings are processed, they will deform after a period
News
Characteristics of metal mold casting process
Metal mold casting is a modern technology of making hollow mold with heat-resistant alloy steel. The metal mold can be
News
Internal casting defects of die casting (part 1)
1 Casting porosity (1) Features and inspection methods: After dissection, appearance inspection or flaw detection showed that the pores had