nodular cast iron

The figure shows the matrix structure of as cast ductile iron. It can be seen from figure a that the […]

The as cast and normalized ductile iron samples were observed with Kearns vh-5000 ultra depth of field optical metallographic microscope.

The test sample bar is taken from the cylindrical nodular cast iron test bar melted in the medium frequency induction

According to the diameter, wall thickness and inspection requirements of the main shaft hole of the wheel hub, the pouring

The nodular iron castings of wind power wheel hub belong to thick and large section castings, especially the thickness of

In order to explore the effect of ultrasonic treatment time on the microstructure and properties of ductile iron, a group

Using 340mm feldspar ink probe, add ultrasound into the spheroidizing bag, the action time is 1min, and the indication of

After spheroidizing, the experimental molten iron is poured into the mold, ultrasonic wave is applied to one of the cavities,

Compared with gray cast iron, nodular cast iron has strict requirements for chemical composition. The raw molten iron of nodular

As shown in Figure 1, the scanning photo of impact fracture micro morphology of B2 sample of nodular cast iron

The composition of nodular cast iron crankshaft obtained from ZHY Casting is shown in the table. Cinnamon sand is used

In order to further study the impact toughness of nodular cast iron for wind power fittings, the impact fracture of

The testing experiments of nodular cast iron wind power castings include chemical composition testing, mechanical property testing, metallographic structure analysis