Effect of silicon solution strengthening on properties of nodular cast iron
1) The strength and elongation properties of y-block hot metal casting were compared. It can be seen that with the […]
Scientific
Scientific
Scientific
Analysis of filling velocity field of gating system for large planetary carrier steel castings
Scheme 1 According to the simulation results in Fig. 1 (E), the whole filling process takes about 19.6 s, which
Scientific
Material control and test method of large vermicular graphite iron castings
In order to control the content of some trace elements (Ti, Pb, etc.) in Vermicular Graphite Cast Iron and ensure
Scientific
Cold bending cracking of martensitic stainless steel castings
The working conditions of hydraulic turbine equipment are strict, and runner, as the core component of hydraulic turbine, has been
Scientific
Control points of cold depth of chilled cast iron camshaft and hardness of cam peach tip
1.Key points of cold depth control (1) cold iron. In the early stage of product development, according to its own
Scientific
Technical requirements for cold depth of chilled cast iron camshaft and hardness of cam peach tip
When the chemical composition and matrix hardness of the hot metal are controlled in the small range mentioned above, the
Scientific
Proportional solidification process of pancake iron castings
1.Analysis of process characteristics Pancake iron castings (diameter and thickness) δ Although the shape of the casting is simple, it
Scientific
Analysis of stress field during solidification process of track shoe in Lost Foam Casting
The solidification process of liquid metal is divided into three phases: liquid phase, solid / liquid phase coexistence and solid
Scientific
Effect of pouring temperature on defects of track shoes in Lost foam Casting Process
In the solidification process, because of the wide range of crystallization temperature, the basic metal skeleton is formed first when
Scientific
Pre treatment of numerical simulation for solidification process of track shoes in EPC Process
Geometric modeling The heat transfer between the liquid metal and the pattern occurs during the filling process Where, ρ P
Scientific
Numerical simulation of solidification process of track shoes in Lost Foam Casting Process Based on ProCAST
Crawler shoe is the key component of roadheader walking mechanism, which is connected by pin to form crawler shoe chain.
Scientific
Formation mechanism of Macrosegregation in reverse squeeze casting
The segregation behavior of impurity elements needs to be analyzed from the aspects of solidification thermodynamics and kinetics. From the
Scientific
Segregation position of impurity elements in large wheel hub in reverse squeeze casting
According to the data in Table 1, the segregation position of each element along the longitudinal direction can be further
Scientific
Segregation degree of impurity elements in large wheel hub by reverse squeeze casting
The contents of impurity elements at different positions in A356 aluminum alloy wheel hub by reverse squeeze casting are shown
Scientific
Experimental method for segregation behavior of impurity elements in large wheel hub by reverse squeeze casting
The test material is A356 aluminum alloy, and its chemical composition is controlled according to American Standard b108-03a. A heavy
Scientific
Inclined pouring process design of top plate casting
The top plate casting is an important part of the supporting transportation equipment for metallurgical vehicles. Its structure is shown
Scientific
Vacuum casting process design of forklift front axle
1 Mold Design According to the overall dimension of the product, the size of sand box is 550 mm ×
Scientific
Production test and product inspection of forklift front axle by vacuum casting
1 Production Process The production process is shown in Fig. 1 ~ 5, including coating spraying, coating drying, core setting,
Scientific
Simulation of casting process for oversize crusher frame
The casting process of crusher frame products is relatively mature, and the process design ideas are generally similar, and the
Scientific
Casting process optimization of ZL104 aluminum alloy cutter body
The cutterhead body produced by the company is made of ZL104 material. The cutterhead body is used to install the
Scientific
Study on properties of vermicular graphite cast iron and its application in internal combustion engine
As for the development of vermicular graphite cast iron technology, in 1948, the Americans applied it. However, due to the
Scientific
Analysis of heat treatment strengthening mechanism of 7075 alloy by rheo squeeze casting
In the process of solid solution, the alloy elements are dissolved into the base metal, the hardness and strength of
Scientific
Mechanical properties and microstructure of rheo SQUEEZE CASTING 7075 alloy after heat treatment
According to the above research and analysis, it is concluded that the best T6 heat treatment process for rheo SQUEEZE
Scientific
Microstructure and properties of 7075 rheo squeeze casting parts aged at different holding time
A number of heat-treated samples with the size of 15 × 15 × 15mm were selected from the successful parts.
Scientific
Microstructure and properties of 7075 rheo squeeze casting parts under different aging conditions
The results show that the strength of 7075 rheo squeeze casting parts can be greatly increased by aging treatment. The
Scientific
Hardness analysis of 7075 rheo squeeze casting parts treated with different solution time
The Brinell hardness values of 7075 rheo squeeze casting samples after solution treatment at different time were counted in the
Scientific
Microstructure of 7075 rheo squeeze casting parts treated with different solution time
After determining 475 ℃ as the best solution temperature, four 15 × 15 × 15mm heat-treated samples were taken from
Scientific
Analysis and discussion of solution treatment experiment results of 7075 rheo squeeze casting parts at different solution temperatures
It can be seen from the metallographic structure figure 1 after solution treatment at different temperatures for 2 h that
Scientific
Hardness analysis of 7075 rheo squeeze casting parts treated with different solution temperature
Hardness test is the most simple and easy method in mechanical property test. In order to replace some mechanical property
Scientific
Microstructure of 7075 rheo squeeze casting parts treated at different solution temperatures
The DSC thermal analysis curve of 7075 aluminum alloy was tested in the experiment. According to the thermal analysis curve,