Process flow and process design of rapid sand casting
The process of rapid sand casting technology to realize the rapid manufacturing of parts is as follows: establish the three-dimensional […]
Scientific
Scientific
Scientific
Internal quality control of sand casting for aluminum alloy cabin door with overall wall thickness of 2 mm
According to the above anti gravity test results, the differential pressure sand casting process was selected to pour the actual
Scientific
Preparation of test nodular cast iron
(1) Raw materials The main ingredients for preparing molten iron in the experiment are Q10 pig iron, scrap steel, spheroidizing
Scientific
Control of dimensional accuracy of sand casting for aluminum alloy cabin door with overall wall thickness of 2 mm
The wall thickness of the hatch sand casting is 2 mm, and the dimensional accuracy requirements are high. It is
Scientific
Mold filling of sand casting for aluminum alloy cabin door with overall wall thickness of 2 mm
The hatch sand castings are sand castings with overall wall thickness of 2 mm. There is no report on the
Scientific
Structural characteristics and technical requirements of sand casting for aluminum alloy hatch with overall wall thickness of 2 mm
The hatch sand casting is a key structural member of aluminum alloy for aircraft. The outline dimension of fad hatch
Scientific
Sand casting process design of large nodular cast iron volute
1. Sand mold casting process scheme of nodular cast iron Nodular cast iron sand castings are produced in single piece
Scientific
Implementation of lost foam forming process scheme for output shaft shell
1. EPS foaming white mold EPS (polystyrene foam) has good mold filling performance, good surface quality, small investment in pre
Scientific
Analysis of lost foam casting process scheme for output shaft shell
According to the forming and manufacturing process of output shaft shell, different casting enterprises adopt different molding lost foam process
Scientific
Solution method of numerical model of solidification process in lost foam casting
According to different discrete methods, the solution methods of numerical model in lost foam casting solidification process mainly include finite
Scientific
Prevention and remedy of common defects in heat treatment process of automobile piston pin parts
1.The concentration of carburized layer is too high Characteristics of heat treatment defects: There are massive carbides or network carbides
Scientific
Analysis of shrinkage porosity in sand castings
The figure shows the results of shrinkage porosity after solidification of sand casting frame, and the criterion of casting shrinkage
Scientific
Heat treatment process of automobile piston pin parts
1. Processing route The machining routes corresponding to different forms of raw materials are different. At present, the forms of
Scientific
Analysis of solidification results of frame sand casting process
The figure shows the solidification fraction of the sand casting frame at different times. It can be seen that the
Scientific
Control of common defects in lost foam casting of aluminum alloy
Aiming at the common defects in the process of aluminum alloy lost foam casting, the following measures have been widely
Scientific
Numerical simulation and analysis process of ball mill liner in lost foam casting
1. Grid division and process parameter setting The three-dimensional modeling software (ugnx6. O) is used to accurately model the liner
Scientific
Lost foam casting ball mill liner based on ProCAST
The size of ball mill liner in lost foam casting should consider the factors such as convenient handling, loading and
Scientific
Optimization of gating system in lost foam casting of gray cast iron thin wall gearbox shell
The lost foam casting thin-walled gray cast iron gearbox shell casting with the improved gating system is adopted. The qualification
Scientific
Lost foam casting process of flywheel
Flywheel is a part of engine components. Its product surface is fully processed. The dynamic balance test of parts. Although
Scientific
Defects in lost foam casting of large diameter thin wall ductile iron watch case
Under the same production conditions, the process yield and scrap rate of three different casting process schemes were obtained. Scheme
Scientific
Production of dual phase steel castings by sand casting
1. Production of heat subsidy for sand casting Mix the powdered heating material and binder evenly according to the required
Scientific
Design of exhaust system for sand core in sand mold casting
The reasonable design of the exhaust system of sand mold casting sand core should comprehensively consider the exhaust hole and
Scientific
Design of exhaust system for sand casting cavity
The design of exhaust system of sand mold cavity can be divided into three parts: pouring riser, air outlet, air
Scientific
Surface microhardness of gray cast iron after graphite annealing
The hardness changes of gray cast iron after laser melting and impact at different annealing temperatures are shown in the
Scientific
Mold filling and solidification characteristics of lost foam casting
Compared with ordinary sand casting, the solidification characteristics of lost foam casting are also different, mainly in the following aspects:
Scientific
Solidification simulation and process optimization of sand casting for large bearing pedestal
Through the analysis of the physical parameters of the sand mold casting, it is determined that the quality of the
Scientific
Casting process of lost foam casting empty shell
1. Foam casting for lost foam casting The molding of polystyrene bead mold can increase the foam density for improving
Scientific
Effect of laser shock on graphitization nucleation of gray cast iron
The nucleation and growth of gray cast iron graphite are gradually formed during heating. The nucleation position of gray cast
Scientific
Sand mold casting process design of large bearing pedestal
The material of the bearing seat is ZG310-570, and the production nature is mass production. 1. Sand casting process scheme
Scientific
XRD of the fused layer of gray cast iron after laser shock
The X-ray diagram of the surface of gray cast iron sample after laser shock melting is as follows. It can