The influence of vibration frequency on the microstructure and properties of gray cast iron in lost foam casting was studied […]

Gray cast iron is mainly composed of matrix structure and graphite, and others include eutectic group, carbide and cementite eutectic.

The figure shows the relationship between Brinell hardness of gray cast iron and sample wall thickness. It can be seen

The figure shows the fracture morphology of grey cast iron prepared under different amplitude conditions. Among them, figures (a) –

When the microcrack propagation no longer depends on the material surface conditions, the crack initiation stage ends, and the crack

The figure shows the austenite morphology of gray cast iron prepared under different vibration frequencies. Figures (a) – (d) show

In order to better study the fatigue wear resistance of gray cast iron brake material, after every 150 thermal cycles,

After the molten iron is poured into the crucible, the temperature of gray cast iron has a stable process, that

The thermal fatigue resistance of materials is closely related to the tensile strength. Figure 1 shows the fracture morphology of

When studying the effect of carbon content on the thermal fatigue performance of laser bionic gray cast iron, the graphite

Generally speaking, the eutectoid transformation starts from the formation of cementite sheet at the austenite grain boundary. The formation and

Change trend of white mouth width of triangular test piece: 5.5mm; 4.6mm ； 3.8mm； All white mouth; All white mouth

Based on the study of gray cast iron brake drum, through the study of various brake drums, it is found

According to the outer contour, the eutectic group of gray cast iron can be divided into three types: spherical eutectic

Of low carbon equivalent gray cast iron modified by rare earth α- The lattice constant of Fe is measured by

It can be seen from the measurement results of free linear shrinkage and its corresponding relationship curve in the table

Figure 1 shows the microstructure changes of gray cast iron matrix and unit without thermal fatigue and 300 thermal cycles.

1. Base metal structure of different graphite types Figure 1 shows the graphite type of no.a-no.e, and its chemical composition

The hardness of low carbon equivalent gray cast iron treated with rare earth is also compared with HT250 inoculated with