Test of QT500-14 and QT600-10 High Silicon Ductile Iron
1.Test result The large number of tests have been carried out according to the above process plan, and the overall […]
Scientific
Scientific
Scientific
Changes of matrix structure of laser modified surface graphitization annealing of gray cast iron
Three kinds of gray cast iron samples annealed after heating to 700 ℃, 800 ℃ and 900 ℃ were tested
Scientific
Graphite morphology of vermicular graphite cast iron in lost foam casting
The effects of vibration frequency and molten iron treatment temperature on graphite morphology and primary phase of vermicular graphite cast
Scientific
Analysis of mechanical properties of nodular cast iron
It can be seen from the table that the tensile strength and impact toughness of nodular cast iron show high
Scientific
Casting solidification field of vermicular cast iron pressure plate
The cloud diagram of solid phase distribution of vermicular cast iron is shown in Figure 1. From the solid phase
Scientific
Melting process of high silicon nodular cast iron
In order to minimize the content of harmful elements, the selected raw materials should be relatively pure, so high-quality pig
Scientific
Production of heavy section ductile iron wind power castings
1. Selection of raw materials Due to the inherent performance characteristics of wind power ductile iron castings, the requirements for
Scientific
Friction and wear test of laser melting layer of gray cast iron
Friction coefficient and wear amount are important parameters to characterize the wear resistance of materials. The higher the surface hardness
Scientific
Effect of amplitude on graphite morphology and primary austenite of vibration lost foam casting gray cast iron
The effects of vibration frequency and amplitude on graphite morphology, primary austenite and properties of vibration lost foam casting gray
Scientific
Fatigue properties of nodular cast iron
At different austenitizing temperatures and isothermal temperatures, the bending fatigue test results of ductile iron specimens at room temperature are
Scientific
Temperature field of compacted vermicular cast iron during mold filling
The pouring conditions of vermicular cast iron pressure plate are as follows: pouring temperature 1419 ℃, pouring speed 0.55m/s, pouring
Scientific
Mesh generation and parameter setting of compacted vermicular cast iron pressure plate model
In ProCAST, tetrahedral mesh model is commonly used for mesh generation. The quality of mesh usually affects the accuracy of
Scientific
Chemical composition selection of High Silicon Ductile Iron
According to the relationship between the elongation and Si content of nodular cast iron, as well as the internal control
Scientific
Test results and discussion of ADC12-0.25Ti aluminum alloy automobile castings
1. Microstructure The microstructure photos of titanium containing aluminum alloy ADC12-0.25Ti samples cast at different temperatures are shown in Figure
Scientific
Microhardness test of laser melting layer of gray cast iron
After laser melting, the microhardness of gray cast iron surface in different areas is divided into three obvious sections, among
Scientific
Tensile test and impact test of nodular cast iron
The tensile test shall be carried out in accordance with gb/t 228-2002 tensile test method for metallic materials at room
Scientific
Low pressure sand casting of aluminum alloy complex thin wall parts
1. Selection of casting method The wall thickness of the casting is thin, the flow resistance of the molten metal
Scientific
QT500-14, QT600-10 High Silicon Ductile Iron
With the development of science and technology and the continuous innovation of cast iron production technology, the ductile iron grades
Scientific
Analysis of impact properties of 30CrNiMo steel castings
According to the results of chemical elements, the chemical composition of steel castings meets the requirements of ZG30CrNiMo steel in
Scientific
Metallographic structure change of melting layer of gray cast iron after laser shock
Fig. 1 corresponds to the cross-sectional morphology of the surface of gray cast iron melting layer after continuous impact of
Scientific
Experimental equipment for composite squeeze casting of large aluminum wheel hub
1. Large hydraulic press Composite squeeze casting is a new squeeze casting method proposed in. At present, there is no
Scientific
Application case of three-dimensional model for riser process of steel castings
Taking the profile bar on a track powered rolling car as an example, the material of the steel casting is
Scientific
Cooling curve of flake graphite cast iron and nodular cast iron
The cooling curves of typical flake graphite cast iron and nodular cast iron are shown in the figure. It can
Scientific
Effect of vibration on hardness of white cast iron
The figure shows the hardness change of white cast iron in lost foam casting with and without vibration. It can
Scientific
Test of nodular cast iron
As cast crankshaft castings with nodular cast iron trademark of QT800-2 are selected as the samples. After testing, the nodularity
Scientific
Sand mold low pressure casting of aluminum alloy complex thin wall parts
Aluminum alloy castings are widely used in railway, military, aerospace, automotive, medical and other fields because of their good comprehensive
Scientific
Physical and chemical inspection of 30CrNiMo steel castings
1. Fractograph The fracture morphology of impact sample was observed by Zeiss evo15 scanning electron microscope. The fracture morphology of
Scientific
Surface residual stress induced by laser shock in gray cast iron
Due to the temperature gradient generated in the process of laser melting of gray cast iron and the transformation of
Scientific
Process flow of composite squeeze casting
According to the definition of composite squeeze casting, the process flow of the composite squeeze casting forming method is as
Scientific
Effect of sample wall thickness on Microstructure of white cast iron
The picture shows the microstructure of white cast iron with different wall thickness. Among them, figures (a) – (c) are