ductile iron casting

Ductile iron casting plays a crucial role in the field of automotive engineering, providing numerous benefits and contributing to the […]

Ductile iron casting is a versatile and widely used casting method in industrial manufacturing. This process offers numerous advantages and

The matrix structure of spheroidal graphite cast iron has a very significant impact on its impact properties. It is the

Today’s wind power technology presents the trend of large-scale development. Larger units can make more intensive use of wind energy

Ductile iron is an important material in strong and tough cast iron. Its strength, plasticity and toughness are higher than

The casting simulation software was used to simulate the mold filling and solidification process of the balance shaft support. Figure

(1) Ductile iron castings have large overall dimensions, high requirements for size and wall thickness control, large wall thickness difference,

The most effective way to solve the internal shrinkage casting defects of nodular iron castings is to use chill and

In the casting process of ductile iron castings, the liquid metal has high viscosity and poor mold filling ability, which

Most excavators work in the open air, and the service environment is poor. The working mechanisms of excavator bucket, stick,

The figure shows the solidification cooling curve of nodular cast iron with different Nb content. It can be seen that

Overall dimension of Puma main cover 182mm × 130mm × It is 63.5mm, 5.4kg, QT500-7, hb170-241. Dimensions of v348 differential

75sife alloy is the most widely used inoculant at home and abroad. The composite inoculant composed of Ca, Ba, Sr

The wall thickness of 100 ton ductile iron nuclear spent fuel container is 520 mm, the hot spot is over

(1) Modulus method: in 1986, when Lin Rui of Harbin University of science and technology was developing the large section

Large section ductile iron has large wall thickness, heavy weight and long solidification time, especially at the center or hot

In order to solve various defects and problems of large section ductile iron castings, scholars at home and abroad have