Common skills of casting runner design
Sand slag hole is the most common surface defect of sand mold casting, which is difficult to avoid and usually […]
Scientific
Scientific
Causes of shrinkage porosity in ductile iron castings
The solidification process of ductile iron castings is generally a process of shrinkage, expansion and re shrinkage. Although the precipitation
Scientific
Selection of casting gate cup and runner shape for automobile disc brake caliper
To obtain a dense casting, the sprue cup should be poured as soon as possible and always filled during the
Scientific
Solidification characteristics of ductile iron casting
Nodular cast iron (ductile iron for short) is the 50th century A kind of high strength cast iron developed in
Scientific
Calculation of casting gating system for automobile disc brake caliper
The flow rate W is defined as the metal weight passing through the cross-sectional area of the gating system within
Scientific
Hot spot / modulus simulation analysis of brake caliper casting parts
Before designing the mold process, the natural properties of the parts should be analyzed, including weight, volume, surface area, number
News
Introduction of vertical parting box less injection molding line for disa casting
Disa company in Denmark is famous for its vertical parting box less injection molding line and shot blasting machine. It
Scientific
Calculation of casting gating system for automobile disc brake caliper
The calculation of flow velocity at specific position of gating system is based on Torricelli formula of ideal free falling
Scientific
Effect of carburizing defect on the composition of gold in lost foam Casting
According to the experimental results of the first two sections, the carburization defects will lead to the excessive chemical composition
News
Problems and research contents in casting process of automobile disc brake caliper
With the application of ductile iron in the global industrial field more and more widely, the quality requirements of ductile
News
Domestic research and application status of casting technology for automobile disc brake caliper
Based on the previous calculation methods and results, some calculation factors have been modified by zhougengao Engineering Co., Ltd., and
Scientific
Analysis of tensile properties of lost foam steel casting
The properties of tensile samples were tested by a universal testing machine controlled by microcomputer, and the tensile strength and
News
Overseas research and application status of casting technology for automobile disc brake caliper
Because of the special solidification property of ductile iron, it is easy to produce shrinkage cavity and shrinkage porosity. How
Scientific
Analysis of volume carburization of steel castings in lost foam casting Process
Six groups of samples were taken when analyzing surface carburization, and the location of the test point was changed to
News
Research significance of casting technology for a kind of automobile disc brake caliper
Automobile brake is the most important part of automobile chassis system, which bears the main responsibility of safe driving. In
Scientific
Analysis of surface carburization of steel castings in lost foam casting Process
In this test, 6 test pieces were poured in the same ladle of molten steel. The chemical composition of molten
News
Study on lost foam casting technology and carburization defect of bridge bearing
By using ProCAST numerical simulation software to study the lost foam casting process of the representative steel and steel bearing
Scientific
Determination of sampling position of carburizing defects in steel castings in lost foam casting Process
In order to study the carburization defects of steel casting for bridge support, four sampling locations are selected, namely, near
News
Study on the effect of carburizing defect on the quality of steel castings
Firstly, the mechanism and manifestation of carburization defects in steel castings are described, and then the experimental methods and main
Scientific
Mechanism of carburizing defect in lost foam steel casting
The filling process of lost foam casting is the replacement process of metal liquid and foam pattern. Because the pouring
Scientific
Verification of lost foam casting process in small batch production
Using the process plan after the second optimization, the small batch production verification of steel and steel bearing was carried
News
Analysis of impact toughness of steel castings in lost foam casting Process
In order to study the impact resistance of steel castings at different temperatures, three temperature detection conditions, namely normal temperature,
Scientific
Analysis of simulation results of lost foam casting process
When setting simulation parameters in ProCAST preprocessing section, the following aspects need to be adjusted: (1) The material of cold
News
Heat treatment technology of lost foam casting
In the process of heating and cooling, there will be group increase transformation of steel, which is the fundamental reason
Scientific
Secondary optimization design of lost foam casting process
The simulation results show that the safety height of riser is 11.15cm, which is 8.15cm higher than the minimum safety
News
Mechanical property index of lost foam casting
Mechanical properties refer to the mechanical characteristics of materials under different environments when they bear various external loads (tensile, compression,
Scientific
Optimization of lost foam casting process parameters and orthogonal test analysis
It can be seen from Fig. 1 that when the pouring temperature changes from high to low, the safe height
News
Experimental route of lost foam casting
The object of this research is steel steel steel bearings in bridge bearings. The production process is produced according to
Scientific
Optimization of lost foam casting process parameters and orthogonal test results
The safety height of riser feeding is taken as the evaluation index in the orthogonal test. The measurement method of
News
Main experimental equipment of lost foam casting
(a) Direct attack spectrometer The main instrument used for chemical composition detection is the direct attack spectrometer (q4-130) in Brooke,